Low Temperature Steell Electrode - - WM - W607

Type of Covering	Equivalent Specification	Welding Position	Type of Current
Low Hydrogen Sodium	AWS E8015-C1 / GB E5515-G1	F, V, OH, H	DC+

Standard & Typical Chemical Composition of Deposited Metal

C	Mn	Si	S	P	Cu	Ni	Mo
≤0.12 0.06	≤1.25 0.90	≤0.60 0.25	≤0.035 0.015	≤0.035 0.015	-	2.00-2.75 2.45	-

Standard & Typical Mechanical properties of Deposited Metal

Y.P(MPa)	T.S(MPa)	El(%)L=5d	Typical I.V(j)
≥440 570	≥540 570	≥17 28	-60℃≥27 90

Applications : Welding of low alloy steel structures for working temperature of which is -60℃,such as 13MnSi6,09MnNiNb,E36, etc.

Low Temperature Steel Electrode - - WM - W707

Type of Covering	Equivalent Specification	Welding Position	Type of Current
Low Hydrogen Sodium	-	F, V, OH, H	DC+

Standard & Typical Chemical Composition of Deposited Metal

C	Mn	Si	S	P	Cu	Ni	Mo
≤0.10	≈0.20	≈0.20	≤0.035	≤0.040	≈0.70	0.70-1.20	-

Standard & Typical Mechanical properties of Deposited Metal

Y.P(MPa)	T.S(MPa)	El(%)L=5d	Typical I.V(j)
-	≥490	≥18	-70℃≥27

Applications : Welding of low alloy steel structures for working temperature of which is -70℃,such as 09Mn2V,09MnTiCuRe, etc.

Low Temperature Steel Electrode - - WM - W707Ni

Type of Covering	Equivalent Specification	Welding Position	Type of Current
Low Hydrogen Sodium	AWS E8015-C1 / GB E5515-G1	F, V, OH, H	DC+

Standard & Typical Chemical Composition of Deposited Metal

C	Mn	Si	S	P	Cu	Ni	Mo
≤0.12 0.06	≤1.25 0.90	≤0.60 0.25	≤0.035 0.010	≤0.035 0.015	-	2.00-2.75 2.40	-

Standard & Typical Mechanical properties of Deposited Metal

Y.P(MPa)	T.S(MPa)	El(%)L=5d	Typical I.V(j)
≥440 490	≥540 590	≥17 25	-70℃≥27 40

Applications : Welding of 3.5%Ni low alloy steel structures for working temperature of which is -70℃.

Low Temperature Steel Electrode - - WM - W907Ni

Type of Covering	Equivalent Specification	Welding Position	Type of Current
Low Hydrogen Sodium	AWS E8015-C2 / GB E5515-C2	F, V, OH, H	DC+

Standard & Typical Chemical Composition of Deposited Metal

C	Mn	Si	S	P	Cu	Ni	Mo
≤0.12 0.06	≤1.25 0.90	≤0.60 0.25	≤0.035 0.010	≤0.035 0.015	-	3.00-3.75 3.30	-

Standard & Typical Mechanical properties of Deposited Metal

Y.P(MPa)	T.S(MPa)	El(%)L=5d	Typical I.V(j)
≥440 520	≥540 620	≥17 25	-90℃≥27

Applications : Welding of 3.5%Ni low alloy steel structures for working temperature of which is -70℃.

Low Temperature Steel Electrode - - WM - W107

Type of Covering	Equivalent Specification	Welding Position	Type of Current
Low Hydrogen Sodium	AWS E7015-C2L/GB E5015-G2L	F, V, OH, H	DC+

Standard & Typical Chemical Composition of Deposited Metal

C	Mn	Si	S	P	Cu	Ni	Mo
≤0.05 0.03	0.50-1.00 0.75	≤0.50 0.25	≤0.035 0.015	≤0.035 0.015	-	3.10-3.70 3.25	-

Standard & Typical Mechanical properties of Deposited Metal

Y.P(MPa)	T.S(MPa)	El(%)L=5d	Typical I.V(j)
≥390 500	≥490 580	≥22 25	-100℃≥27

Applications : Welding of 3.5%Ni low alloy steel structures for working temperature of which is -100℃.

Low Temperature Steel Electrode - - WM - W107Ni

Type of Covering	Equivalent Specification	Welding Position	Type of Current
Low Hydrogen sodium	-	F, V, OH, H	DC+

Standard & Typical Chemical Composition of Deposited Metal

C	Mn	Si	S	P	Cu	Ni	Mo
≤0.08 0.06	≈0.50 0.50	≤0.30 0.20	≤0.020 0.010	≤0.020 0.015	≈0.50 0.30	4.00-5.50 5.20	≈0.30 0.30

Standard & Typical Mechanical properties of Deposited Metal

Y.P(MPa)	T.S(MPa)	El(%)L=5d	Typical I.V(j)
≥340	≥490	≥16	-100℃≥27

Applications : Welding of 06AlNbCuN, 06MnNb and 3.5%Ni steels.